Thermal spray powder - United Coatings Technologies Co., Ltd.

Pure Metal

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF101	Al 99 Gas atomized	90/45μm	CP	Repairing of aluminum and magnesium-based workpieces Resistant to atmospheric, coastal and industrial corrosion EMI shielding Max. service temp. 160°C (320°F)	--
LF121	Ti 99.5 Gas atomized	180/53μm	VP	Bond coat for hydroxyapatite coatings Biocompatibility for medical applications High porosity coating Fire alert Service temp. up to 400 °C (752 °F)	--
LF131	Cu 99 Gas atomized	90/45μm	CP	Repairing of copper based workpieces Conductivity EMI shielding Resistant to inks corrosion Service temp. up to 150 °C (302°F)	--
LF145	Mo 99.5 Agglomerated & Densified	90/38μm	CP	Piston rings, synchronizing rings, valves, pumps and mating parts. Resistant to fretting and electric arc erosion Good bonding Service temp. up to 320 °C (610°F)	--
LF151	W 99 Reduction	75/45μm	AP VP	Corrosion resistant coatings Nozzle and tail cone of rocket engine, and fire-resistant crucible for metal melting Good adhesion to graphite, alumina and quartz Max. service temp. 1,000°C (1,832 °F)	--
LF152	Cr 99.5 Electrolyzed	180/75μm	AP	Sputtering target Resistant to etching With potential health hazard Max. service temp.800°C (1,472°F)	--
LF200	Ni 99.3 Atomized	75/45μm	CP AP	Repair nickel-base workpiece or dimension restoring Coating is dense, easy to machine and corrosion resistant Can be used as bondcoat of ceramic coatings Can be used on EMI and sputtering target Max service temp. 500°C (932°F)	--
LF239	Si 99.9 Fused	45/15μm	AP	With low thermal expansion coefficient and excellent thermal shock resistance With high thermal stability EBC bond coat for CMCs Semiconductor and sputtering targets Service temp. up to 1000 °C (1,832 °F)	--

Fe Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF155	Fe3Al3Mo3CB Clad	106/45μm	CP, AP	Repairing of iron based parts, and crank journals Service temp. up to 300°C (570 °F)	--
LF157	Fe 12Cr 0.15C (420 Stainless Steel) Water atomized	106/45μm	CP, AP	420 stainless steel Mainly suitable for repairing and wearing applications that require a hard ground finish HRc52-55 Service temp. up to 600°C (1,100 °F)	--
LF158	Fe 17Cr 12Ni 3Mo2.3Si 0.03C (316 Stainless Steel) Water atomized	106/45μm	CP, AP	316 stainless steel For protection against corrosion and erosion, and for salvage and repair For protection against seawater environment corrosion HRc23 Service temp. up to 700°C (1,292 °F)	--
LF159	Fe17Cr11Mo3Ni3Si3Cu4B Clad	45/6μm	CP, HV	Corrosion resistant coatings Service temp. up to 600°C (1,110 °F)	--
LF160	Fe 16Mo 2C 0.25Mn Clad	90/11μm	CP, AP	Low-price alternative of hard chromium plating Hard-face support coating Wth low friction coefficient With good corrosion and wear resistance Service temp. up to 350°C (662 °F)	--
LF162	Fe37Ni6Al Clad	106/45μm	AP	Forming high quality metallurgical bonding due to exothermic reaction occurred upon spraying Coating machinable Resistant to high temperature oxidation Service temp. up to 815°C (1,500 °F)	--
LF163	Fe35NiMoAl Clad	125/45μm	CP, AP	Hard coatings Good resistance to oxidation and hot corrosion For salvage and restoration of ferrous alloys For parts of diesel engine Service temp. up to 815°C (1,500 °F)	--
LF165	Fe14WNiCr Clad	125/45μm	AP	Of high shearing strength, Usable for the friction plate of both tank and bulldozer, and the synchronizing ring of automobiles Max. service temp. 500°C(932°F)	--
LF166C	Fe20Cr7B0.5Si Gas atomized	175/89μm	SF, LC	Forming dense and hard coating With good resistance to wear and corrosion Max. service temp. 980°C (1,796°F)	--
LF166F	Fe20Cr7B0.5Si Gas atomized	106/45μm	SF, AP	Forming dense and hard coatings With good resistance to wear and corrosion Suitable for extruder screw of plastic manufacturing industry Max. service temp. 980°C (1,796°F)	--

Mo Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF143	Mo3C Clad	106/45μm	AP	With good toughness and high hardness With good resistance to sliding wearing Service temp. up to 320°C (610 °F)	--
LF144	Mo25Ni (NiCrBSiFe) Blended	90/25μm	CP, SF, AP	Self-fluxing powder With good resistance to abrasion, and low friction coefficient Service temp. up to 350°C (660 °F)	--
LF147	Mo50(NiAlMo)12.5(NiCrBSiFe) Blended	90/45μm	AP	With good resistance to abrasion With low friction coefficient, which is good for piston ring of auto industry Service temp. up to 550°C (1,022 °F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF143

Mo3C

Clad

106/45μm

AP

With good toughness and high hardness
With good resistance to sliding wearing
Service temp. up to 320°C (610 °F)

--

LF144

Mo25Ni (NiCrBSiFe)

Blended

90/25μm

CP, SF, AP

Self-fluxing powder
With good resistance to abrasion, and low friction coefficient
Service temp. up to 350°C (660 °F)

--

LF147

Mo50(NiAlMo)12.5(NiCrBSiFe)

Blended

90/45μm

AP

With good resistance to abrasion
With low friction coefficient, which is good for piston ring of auto industry
Service temp. up to 550°C (1,022 °F)

--

Ni Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF201	Ni5Al Clad	90/45μm	CP, AP	Self-adhesion bondcoat powder for ceramic and abradable top coatings Exothermic reaction occurred during spraying creates excellent self-bonding coating which is dense and machinable Resistant to high temperature oxidation and abrasion For salvage and build-up on carbon and corrosion resistant steels Service temp. up to 800°C (1,470 °F)	--
LF203	Ni18Al Clad	125/45μm	CP, AP	Self-adhesion bondcoat powder for ceramic and abradable top coatings Exothermic reaction occurred during spraying creates excellent self-bonding coating which is dense and machinable Resistant to high temp. oxidation and abrasion For build-up on machinable carbon and corrosion resistant steels Service temp. up to 650°C (1,200 °F)	--
LF204	Ni20Al Chemicallly Clad	90/45μm	CP AP	Self-adhesion bondcoat powder for ceramic and abradable top coatings Exothermic reaction occurred during spraying creates excellent self-bonding coating which is dense and machinable Resistant to high temp. oxidation and abrasion For build-up on machinable carbon and corrosion resistant steels Service temp. up to 650°C (1,200 °F)	--
LF207	Ni20Cr Gas Atomized	106/45μm	CP, AP	Resistant to high temp. oxidizing and corrosive gases, and prevents scaling on carbon and low alloy steels Forming good bondcoat for ceramic top coats Higher chromium enhances corrosion resistance Sputtering target powder or as bond coat Service temp. up to 980°C (1,800 °F)	--
LF210	Ni16Cr8Fe Water atomized	125/45μm	CP, AP	Repairing of nickel based alloy workpieces Corrosion resistant coating with moderate hardness Service temp. up to 650°C (1,200 °F)	--
LF211	Ni9Cr5Al5Mo Clad	125/45μm	CP, AP	Bond coating With good processing performance Resistance to oxidation and corrosion Service temp. up to 750°C (1,380 °F)	--
LF212	Ni18.8Cr6Al Clad	125/45μm	CP, AP	Resistant to oxidation and corrosion Bond coat of ceramic coating For repairing and building up worn or mis-machined nickel, nickel alloy or machinable corrosion resistant steel parts. Service temp. up to 800°C (1,472 °F)	--
LF212Y	Ni22Cr10AlY Gas Atomized	106/53μm	AP	Resistant to high temperature oxidation Bond coat of thermal barrier and oxide ceramic abradable coating High temperature corrosion resistance for turbine engine component, heat treatment fixtures, exhaust manifolds and ducts Service temp. up to 1050°C (1,920 °F)	--
LF213	Ni18.2Cr5Al3CoY Clad	106/53	AP	For high temperature bond coats or salvage of worn/mismachined parts Service temp. up to 980°C (1,800 °F)	--
LF214	Ni18Cr7Al5Mo Clad	125/45μm	CP, AP	Hard stainless steel With good resistance to oxidation and corrosion Forming dense and self-adhesion coating Usable on repairing or build-up of worn stainless steel parts Service temp. up to 750°C (1,380 °F)	--
LF223	Ni5Mo5.5 Al Clad	90/45μm	CP, AP	Self-adhesion Forming coatings with high toughness and fairly hard Resistant to erosion and shock Usable for protecting machine parts, like bearing seals and valves Service temp. up to 800°C (1,472 °F)	--
LF232	Ni31B9C Clad	45/15μm	AP, HV	Forming wear resistant coatings with wearing resistant performance better than metal ceramics like Al₂O₃, Cr₃C₂ and TiC Service temp. up to 800°C (1,472 °F)	--
LF233	Ni30Cu Clad	106/45μm	CP AP	With good resistance to corrosion and high temperature With good thermal conductivity and can be used for slide guide of machine tool With good resistance to seawater, atmospheric and acidic corrosion EMI shielding Service temp. up to 300°C (572 °F)	--
LF234	Ni75Al2O3 Clad	106/45μm	AP	Resistant to corrosion, high temperature, oxidation and thermal shock Service temp. up to 800°C (1,472 °F)	--
LF235	Ni25MoS2 Clad	75/38μm	AP	Forming anti-friction coating With good lubricity, and good chemical and thermal stability Usable as motive seal and low friction material Usable as lubricant coatings Service temp. up to 600°C (1,112 °F)	--
LF236	Ni(20-25) diamond Clad	75/38μm	AP	With high hardness, and resistance to wearing and erosion Usable as wearing and cutting material Usable as filler in powder metallurgy Service temp. up to 350°C (662 °F)	--
LF237	Ni50Cr Gas Atomized	106/38μm	AP	Resistance to high temperature oxidation Resistance to sulfur vanadium corrosion Usable for corrosion prevention of oil and coal burning boiler, with corrosion resistance performance better than 45CT Usable as bond coat for ceramic top coat Service temp. up to 1,000°C (1,832 °F)	--

Al Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF102	Al 10Si Atomized	106/45μm	AP AC	Sputtering target coating use Used to repair aluminum and magnesium alloy parts Better abrasion resistance than pure aluminum Service temp. up to 350°C (662 °F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF102

Al 10Si

Atomized

106/45μm

AP AC

Sputtering target coating use
Used to repair aluminum and magnesium alloy parts
Better abrasion resistance than pure aluminum
Service temp. up to 350°C (662 °F)

--

Co Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF240-1	Co 25.5Cr 10.5Ni 7.5W 0.5C Gas Atomized	106/45μm	CP	Similar to stellite alloy Forming abrasion, fretting and particle erosion resistant coatings Usable for surface restoration of worn cobalt alloy parts Usable on coatings of airfoils and combustors of turbines Service temp. up to 840°C (1,550 °F)	--
LF240-2	Co 25.5Cr 10.5Ni 7.5W 0.5C Gas Atomized	45/15μm	HV	Usable for surface restoration of worn cobalt alloy parts Usable on coatings of airfoils and combustors of turbines Service temp. up to 840°C (1,550 °F)	--
LF241	Co 25Cr 5Al 0.27Y 1.75Si 15hBN Blended	178/10μm	CP, AP	Combats fretting on blade roots of compressor Compatible with titanium blades Effective on large blades under high stress in service Superior performance compared to CuNiIn coatings Service temp. up to 450°C (840 °F)	--
LF242	Co 32Ni 21Cr 8Al 0.5Y Gas Atomized	90/45μm	CP AP	Excellent balance of oxidation，hot corrosion and sulfidation resistance Excellent as a corrosion resistant bond coat Service up to 850℃（1560℉） Can be post-coat heat treated for improved performance	--

Cu Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF132	Cu 10Al Clad	106/45μm	CP	Good dry running performance Some oxidation, wear and fretting resistance For build-up and repair of copper alloy parts Typically used on pumps (cavitation control), piston guides, shifter forks and compressor air seals Service temp. up to 300°C (572 °F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF132

Cu 10Al

Clad

106/45μm

CP

Good dry running performance
Some oxidation, wear and fretting resistance
For build-up and repair of copper alloy parts
Typically used on pumps (cavitation control), piston guides, shifter forks and compressor air seals
Service temp. up to 300°C (572 °F)

--

Standard

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF215	Ni 7.5Cr 3.5Si 2.5Fe 1.7B 0.25C Gas Atomized	125/53μm	CP, SF	LF215 is a kind of self-fluxing Ni 25 powder with hardness of HRc25-30, the coating it forms is machinable Forming dense and hard coatings with ability to resist wear caused by abrasive grains, hard surfaces, particle erosion and cavitation at both low and high temperatures Usable for fuel rod mandrels, thread guides, hot forming dies, oil field tools, hot crushing rolls, forging tools extrusion dies, screw conveyors, chip breakers and shafts, etc. Service temp. up to 500°C (932 °F)	--
LF216	Ni 11Cr 3.7Si 2.75Fe 2.2B 0.5C Gas Atomized	125/45μm	CP, SF	LF216 is a kind of self-fluxing Ni50 powder with hardness of HRc40-45 Forming dense and hard coatings with ability to resist wear caused by abrasive grains, hard surfaces, particle erosion and cavitation at both low and high temperatures Usable for fuel rod mandrels, thread guides, hot forming dies, oil field tools, hot crushing rolls, forging tools extrusion dies, screw conveyors, chip breakers and shafts, etc. Service temp. up to 500°C (932 °F)	--
LF217	Ni 17Cr 4Fe 4Si 3.5B 1C Gas Atomized	106/45μm	CP, SF	LF217 is a kind of self-fluxing Ni60 powder with hardness of HRc58-62 Forming dense and hard coatings with ability to resist wear caused by abrasive grains, hard surfaces, particle erosion and cavitation at both low and high temperatures Usable for fuel rod mandrels, thread guides, hot forming dies, oil field tools, hot crushing rolls, forging tools extrusion dies, screw conveyors, chip breakers and shafts, etc. Service temp. up to 500°C (932 °F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF215

Ni 7.5Cr 3.5Si 2.5Fe 1.7B 0.25C

Gas Atomized

125/53μm

CP, SF

LF215 is a kind of self-fluxing Ni 25 powder with hardness of HRc25-30, the coating it forms is machinable
Forming dense and hard coatings with ability to resist wear caused by abrasive grains, hard surfaces, particle erosion and cavitation at both low and high temperatures
Usable for fuel rod mandrels, thread guides, hot forming dies, oil field tools, hot crushing rolls, forging tools extrusion dies, screw conveyors, chip breakers and shafts, etc.
Service temp. up to 500°C (932 °F)

--

LF216

Ni 11Cr 3.7Si 2.75Fe 2.2B 0.5C

Gas Atomized

125/45μm

CP, SF

LF216 is a kind of self-fluxing Ni50 powder with hardness of HRc40-45
Forming dense and hard coatings with ability to resist wear caused by abrasive grains, hard surfaces, particle erosion and cavitation at both low and high temperatures
Usable for fuel rod mandrels, thread guides, hot forming dies, oil field tools, hot crushing rolls, forging tools extrusion dies, screw conveyors, chip breakers and shafts, etc.
Service temp. up to 500°C (932 °F)

--

LF217

Ni 17Cr 4Fe 4Si 3.5B 1C

Gas Atomized

106/45μm

CP, SF

LF217 is a kind of self-fluxing Ni60 powder with hardness of HRc58-62
Forming dense and hard coatings with ability to resist wear caused by abrasive grains, hard surfaces, particle erosion and cavitation at both low and high temperatures
Usable for fuel rod mandrels, thread guides, hot forming dies, oil field tools, hot crushing rolls, forging tools extrusion dies, screw conveyors, chip breakers and shafts, etc.
Service temp. up to 500°C (932 °F)

--

Blend with Hardfacing Alloys

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF253	35 (WC 12Co) 65(Ni 17Cr 4Fe 4Si 3.5B 1C) Blended	53/15μm	AP, CP, SF	Self-fluxing; usable for post-coat fusing for dense, virtually porosity free and metallurgically bonded coatings Hardness 63-65 Resistant to particle erosion and abrasion Less brittle and lower tendency to crack Less hard than LF340 Used on die mould Service temp. up to 540°C (1,000°F)	--
LF255	50(Ni 5.8Cr 0.7Al 1.4Fe 1.4Si 1.3B 0.3C)-50(WC 12C Blended	75/11μm	AP SF	Self-fluxing, usable for where fusing is not desirable, e.g. thin-walled components and components that may distort if fused For digesters, liquor tanks, manifolds and centrifugal fans in coal or oil plants Service temp. up to 500°C (930°F)	--
LF256	WC/W2C 17Ni 50(Ni 11Cr 2.5Fe 2.5Si 2.5B 0.5C) Clad Blended	90/11μm	SF	Cast tungsten carbide clad with Nickel powder makes the hard particles of WC evenly distributed in the structure, and then well fused with Ni self-fluxing alloy, enabling the powder to have the highest wear and corrosion resistance Hardness 63-68 Usable on extruder screw and screw conveyer of plastic industry Working temp. <900°C (1,652°F)	--
LF258	Ni45(FeCrB) Blended	45/15μm	SF	Resistance to abrasion wear and corrosion With high mechanical strength, and hardness of Hv900-1,300 Recommend for using on screw extruder of plastic industry, Service temp. up to 500°C (930°F)	--

WC Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF321	WC 12Co Sintered & Crushed	45/15μm	HV, AP	Resistant to abrasion and erosion; and good resistance to sliding wear and fretting Hard and dense coating with good bonding For machine parts, pump housings and blades, etc. HV1,050-1,250 by HVOF Service temp. up to 500°C (930°F)	--
LF322-1	WC 12Co Agglomerated & Sintered (Spheroidal)	30/5μm (HVAF)	HV	Coarse WC initial particles Coating formed exhibits good all-around resistance to sliding wear, impact, abrasion and fretting Hard and dense coating with good bonding For dry environments Used for Zn bath rolls in continuous galvanizing lines, and for oil field apparatus, steel rolls, sink rolls, ball valves, exhaust fans, pump housings, conveyor screws and sucker rod couplings, etc. HVOF or HVAF application Service temp. up to 500°C (930°F)	--
LF322-2	WC 12Co Agglomerated & Sintered (Spheroidal)	45/15μm (Kerosene)	HV	Coarse WC initial particles Coating formed exhibits good all-around resistance to sliding wear, impact, abrasion and fretting Hard and dense coating with good bonding For dry environments Used for Zn bath rolls in continuous galvanizing lines, and for oil field apparatus, steel rolls, sink rolls, ball valves, exhaust fans, pump housings, conveyor screws and sucker rod couplings, etc. HVOF or HVAF application Service temp. up to 500°C (930°F)	--
LF322-3	WC 12Co Agglomerated & Sintered (Spheroidal)	53/11μm (Gas Fuel)	HV	Coarse WC initial particles Coating formed exhibits good all-around resistance to sliding wear, impact, abrasion and fretting Hard and dense coating with good bonding For dry environments Used for Zn bath rolls in continuous galvanizing lines, and for oil field apparatus, steel rolls, sink rolls, ball valves, exhaust fans, pump housings, conveyor screws and sucker rod couplings, etc. HVOF or HVAF application Service temp. up to 500°C (930°F)	--
LF323-1	WC 12Co Agglomerated & Sintered (Spheroidal)	38/10μm (HVAF)	HV AP	Coarse WC initial particles Coating formed exhibits good all-around resistance to sliding wear, impact, abrasion and fretting Hard and dense coating with good bonding For dry environments, Used for Zn bath rolls in continuous galvanizing lines, and for oil field apparatus, steel rolls, sink rolls, ball valves, exhaust fans, pump housings, conveyor screws and sucker rod couplings, etc. HVOF or HVAF application Service temp. up to 500°C (930°F)	--
LF323-2	WC 12Co Agglomerated & Sintered (Spheroidal)	45/15μm (Kerosene)	HV AP	Made from Medium WC initial particles Hard and dense coatings with good resistance to abrasion, erosion and sliding wear Coating formed is smooth with fine micro-structure and high bonding strength Used for wire drawing and agricultural equipment Service temp. up to 500°C (930°F)	--
LF323-3	WC 12Co Agglomerated & Sintered (Spheroidal)	45/11μm (Gas Fuel)	HV AP	Made from Medium WC initial particles Hard and dense coatings with good resistance to abrasion, erosion and sliding wear Coating formed is smooth with fine micro-structure and high bonding strength Used for wire drawing and agricultural equipment Service temp. up to 500°C (930°F)	--
LF324-1	WC 12Co Agglomerated & Sintered (Spheroidal)	30/5μm (HVAF)	HV	Fine WC initial particles Coating formed is resistant to sliding wear, hammer (impact) wear, abrasion and fretting Higher apparent density and finer roughness Ideal for corrugating rolls Coating formed is dense with smooth surface Service temp. up to 500°C (930°F)	--
LF324-2	WC 12Co Agglomerated & Sintered (Spheroidal)	45/15μm (Kerosene)	HV	Fine WC initial particles Coating formed is resistant to sliding wear, hammer (impact) wear, abrasion and fretting Higher apparent density and finer roughness Ideal for corrugating rolls Coating formed is dense with smooth surface Service temp. up to 500°C (930°F)	--
LF324-3	WC 12Co Agglomerated & Sintered (Spheroidal)	45/11μm (Gas Fuel)	HV	Fine WC initial particles Coating formed is resistant to sliding wear, hammer (impact) wear, abrasion and fretting Higher apparent density and finer roughness Ideal for corrugating rolls Coating formed is dense with smooth surface Service temp. up to 500°C (930°F)	--
LF329-1	WC 17Co Agglomerated & Sintered (Spheroidal)	30/5μm (HVAF)	HV, AP	Higher ductility than WC-Co 88/12 due to higher Co content Hard and dense coatings with good resistance to sliding and impact wear Used for extrusion dies, glass industry, paper mill rolls, pump parts, wire drawing equipment and wing skids of airplanes etc. With a relatively poor performance in resisting oxidation and corrosion Service temp. up to 500°C (930°F)	--
LF329-2	WC 17Co Agglomerated & Sintered (Spheroidal)	45/11μm (Gas Fuel HVOF or APS)	HV, AP	Higher ductility than WC-Co 88/12 due to higher Co content Hard and dense coatings with good resistance to sliding and impact wear Used for extrusion dies, glass industry, paper mill rolls, pump parts, wire drawing equipment and wing skids of airplanes etc. With a relatively poor performance in resisting oxidation and corrosion Service temp. up to 500°C (930°F)	--
LF329-3	WC 17Co Agglomerated & Sintered (Spheroidal)	45/11μm (Gas Fuel HVOF or APS)	HV, AP	Higher ductility than WC-Co 88/12 due to higher Co content Hard and dense coatings with good resistance to sliding and impact wear Used for extrusion dies, glass industry, paper mill rolls, pump parts, wire drawing equipment and wing skids of airplanes etc. With a relatively poor performance in resisting oxidation and corrosion Service temp. up to 500°C (930°F)	--
LF332	WC 17Ni Agglomerated & Sintered	45/10μm	AP, HV	Clad, a wear-resistant coating with a better corrosion stability than WC-12Co and a lower hardness Service temp. up to 500°C (930°F)	--
LF335	WC20Cr3C27Ni Agglomerated & Sintered	45/10μm	AP, HV	With better performance than WC-Co in resisting oxidation and corrosion With strong strength and good microstructure, and used for gates and valves Service temp. up to 700°C (1,290°F)	--
LF337	(WC12Co)35(Cr3C2 20NiCr) Agglomerated & Sintered	45/6μm	AP, HV	Substitute of hard chromium plating Resistant to corrosion, wear resistant and fretting Service temp. up to 700°C (1,290°F)	--
LF338-1	WC10Co4Cr Agglomerated & Sintered (Spheroidal)	30/5μm (HVAF)	HV, AP	Substitute of hard chromium plating Coating formed shows good corrosion stability, good resistance to wear and erosion, and with a highly polished surface Used for moist corrosion environment, landing gears, paper manufacturing industry, hydro plant parts, hydraulic cylinders, shafts, actuators, pump seals and valves, etc. Service temp. up to 500°C (930°F)	--
LF338-2	WC10Co4Cr Agglomerated & Sintered (Spheroidal)	45/15μm (Kerosene)	HV, AP	Substitute of hard chromium plating Coating formed shows good corrosion stability, good resistance to wear and erosion and with a highly polished surface Used for moist corrosion environment, landing gears, paper manufacturing industry, hydro plant parts, hydraulic cylinders, shafts, actuators, pump seals and valves, etc. Service temp. up to 500°C (930°F)	--
LF338-3	WC10Co4Cr Agglomerated & Sintered (Spheroidal)	45/11μm (Gas fuel HVOF)	HV, AP	Substitute of hard chromium plating Coating formed shows good corrosion stability, good resistance to wear and erosion, and with a highly polished surface Used for moist corrosion environment, landing gears, paper manufacturing industry, hydro plant parts, hydraulic cylinders, shafts, actuators, pump seals and valves, etc. Service temp. up to 500°C (930°F)	--
LF339-1	WC10Co4Cr Sintered Crushed	35/5μm (HVAF)	HV, AP	Substitute of hard chromium plating Resistant to corrosion, wear and wet environment corrosion, and used for moist corrosion environment Better resistance to corrosion and cavitation than WC-Co coatings Coating formed is very dense Used for ball valves, landing gears, paper manufacturing industry, hydro plant parts and hydraulic cylinders Service temp. up to 500°C (930°F)	--
LF339-2	WC10Co4Cr Sintered Crushed	45/15μm (Kerosene)	HV, AP	Substitute of hard chromium plating Resistant to corrosion, wear and wet environment corrosion, and used for moist corrosion environment Better resistance to corrosion and cavitation than WC-Co coatings Coating formed is very dense Used for ball valves, landing gears, paper manufacturing industry, hydro plant parts and hydraulic cylinders Service temp. up to 500°C (930°F)	--
LF339-3	WC10Co4Cr Sintered Crushed	53/10μm (Gas fuel HVOF)	HV, AP	Substitute of hard chromium plating Resistant to corrosion, wear and wet environment corrosion, and used for moist corrosion environment Better resistance to corrosion and cavitation than WC-Co coatings Coating formed is very dense Used for ball valves, landing gears, paper manufacturing industry, hydro plant parts and hydraulic cylinders Service temp. up to 500°C (930°F)	--
LF340	WC 9Co 5Cr 1Ni Agglomerated & Sintered	45/10μm	HV, AP	High resistance to corrosion and abrasion Excellent alternative to hard chromium, particularly in HCl media For mining carrier belt rollers, paper machinery rollers, slush pump rods, dump valves, pump seals and hydraulic rods, etc. Service temp. up to 500°C (930°F)	--
LF341	WC20Cr7Ni Agglomerated & Sintered	45/10μm	HV, AP	Forming dense coatings with high hardness and tenacity as well as good corrosion stability for organic acid and alkali liquor Used for oil field equipment, chemical industry, compressor shaft, hydraulic machine case, papermaking roller and gas delivery equipment Service temp. up to 500°C (930°F)	--
LF342	W2C / WC 12Ni Clad Blended	53/10μm	HV	Coating formed is hard and dense and with general resistance to abrasion wear Service temp. up to 450°C (842°F)	--
LF361	TiC12Ni Clad	45/15μm	HV	Forming harder coatings with better resistance to abrasion and less expensive in comparison with WC-12Co Not suitable for use in wet and corrosive environment Service temp. up to 450°C (842°F)	--
LF362	TiC28Co8Cr Agglomerated & Sintered	45/15μm	HV	Forming harder coatings with better resistance to abrasion and less expensive in comparison with WC-10Co-4Cr Usable in wet and corrosive environment Service temp. up to 450°C (842°F)	--

Cr3C2 Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF301F	Cr3C2 Sintered & Crushed	106/30μm	AP	High microhardness (1,200HV₃₀₀) and wear resistance at elevated temperatures Choose higher carbide content for higher hardness and resistance to fretting, abrasion and particle erosion For turbine components: air seals, baffle dampers, nozzle supports, valve seats, struts For hot crushing rolls, forming dies, forging tools Service temp. up to 870°C (1,600°F)	--
LF302	Cr3C2 7(Ni20Cr) Blended	45/5μm	AP HV	High microhardness (1,200HV₃₀₀) and wear resistance at elevated temperatures Choose higher carbide content for higher hardness and resistance to fretting, abrasion and particle erosion For turbine components: air seals, baffle dampers, nozzle supports, valve seats, struts For hot crushing rolls, forming dies, forging tools Service temp. up to 870°C (1,600°F)	--
LF303	Cr3C2 10(Ni20Cr) Blended	45/5μm	AP HV	High microhardness (1,200HV₃₀₀) and wear resistance at elevated temperatures Choose higher carbide content for higher hardness and resistance to fretting, abrasion and particle erosion For turbine components: air seals, baffle dampers, nozzle supports, valve seats, struts For hot crushing rolls, forming dies, forging tools Service temp. up to 870°C (1,600°F)	--
LF304	Cr3C2 25(Ni 20Cr) Blended	45/5μm	AP HV	High microhardness (1,200HV₃₀₀) and wear resistance at elevated temperatures Choose higher carbide content for higher hardness and resistance to fretting, abrasion and particle erosion For turbine components: air seals, baffle dampers, nozzle supports, valve seats, struts For hot crushing rolls, forming dies, forging tools Service temp. up to 870°C (1,600°F)	--
LF305	Cr3C2 17Ni Clad	45/10μm	HV AP	Coarse dense carbide Excellent resistance to severe abrasive and fretting wear Recommended for protection of cavitation and sliding wear at higher temperatures Good resistance to solid particle erosion Max. operating temperature 870°C (1,600°F)	--
LF307	Cr3C2 25（Ni20Cr） Agglomerated & Sintered	38/10μm	HV	Good resistance to oxidation, abrasion, particle erosion, fretting, cavitation, hot gas corrosion, high temperature corrosion, tribocorrosion Excellent alternative to hard chromium plating with better resistance to chloride, acidic and alkaline Good sliding properties and cavitation resistance Used in pump housing, machine parts, hydraulic valves, tools, hot forming dies, etc. Max. operating temperature 870°C (1,600°F)	--
LF307-1	Cr3C2 25(Ni20Cr) Agglomerated & Sintered (Spheroidal)	30/5μm (HVAF)	HV	Good resistance to oxidation, abrasion, particle erosion, fretting, cavitation, hot gas corrosion, high temperature corrosion, tribocorrosion Excellent alternative to hard chromium plating with better resistance to chloride, acidic and alkaline Good sliding properties and cavitation resistance Used in pump housing, machine parts, hydraulic valves, tools, hot forming dies, etc. Max. operating temperature 870°C (1,600°F)	--
LF307-2	Cr3C2 25(Ni20Cr) Agglomerated & Sintered (Spheroidal)	45/15μm (Kerosene)	HV	Good resistance to oxidation, abrasion, particle erosion, fretting, cavitation, hot gas corrosion, high temperature corrosion and tribocorrosion Excellent alternative to hard chromium plating with better resistance to chloride, acidic and alkaline Good sliding properties and cavitation resistance Used in pump housing, machine parts, hydraulic valves, tools and hot forming dies, etc. Max. operating temperature 870°C (1,600°F)	--
LF307-3	Cr3C2 25(Ni20Cr) Agglomerated & Sintered (Spheroidal)	45/11μm (Gas Fuel HVOF)	HV	Good resistance to oxidation, abrasion, particle erosion, fretting, cavitation, hot gas corrosion, high temperature corrosion and tribocorrosion Excellent alternative to hard chromium plating with better resistance to chloride, acidic and alkaline Good sliding properties and cavitation resistance Used in pump housing, machine parts, hydraulic valves, tools and hot forming dies, etc. Max. operating temperature 870°C (1,600°F)	--
LF308	Cr3C2 25(Ni20Cr) Blended	106/10μm	HV	Good resistance to oxidation, abrasion, particle erosion, fretting, cavitation, hot gas corrosion and high temperature corrosion Excellent alternative to hard chromium plating with better resistance to chloride, acidic and alkaline Good sliding properties and cavitation resistance Used in pump housing, machine parts, hydraulic valves, tools and hot forming dies, etc. Less expensive than LF308 due to blending method Max. operating temperature 870°C (1,600°F)	--
LF309-1	Cr3C2 20(Ni20Cr) Agglomerated & Sintered (Spheroidal)	30/5μm (HVAF)	HV	Excellent resistance to severe abrasive and fretting wear Recommended for protection of cavitation and sliding wear at higher temperatures Good resistance to solid particle erosion Higher hardness than 75:25 LF307 and LF308 Max. operating temperature 870°C (1,600°F)	--
LF309-2	Cr3C2 20(Ni20Cr) Agglomerated & Sintered (Spheroidal)	45/15μm (Kerosene)	HV	Excellent resistance to severe abrasive and fretting wear Recommended for protection of cavitation and sliding wear at higher temperatures Good resistance to solid particle erosion Higher hardness than 75:25 LF307 and LF308 Max. operating temperature 870°C (1,600°F)	--
LF309-3	Cr3C2 20(Ni20Cr) Agglomerated & Sintered (Spheroidal)	45/11μm (Gas Fuel)	HV	Excellent resistance to severe abrasive and fretting wear Recommended for protection of cavitation and sliding wear at higher temperatures Good resistance to solid particle erosion Higher hardness than 75:25 LF307 and LF308 Max. operating temperature 870°C (1,600°F)	--
LF310	Cr3C2 35(Ni20Cr) Agglomerated & Sintered (Spheroidal)	58/10μm	HV	Lower hardness than ratio 75/25 LF307 and LF308 Max. operating temperature 870°C (1,600°F)	--
LF312	Cr3C2 25(NiCrAlY) Blended	45/10μm	AP	Good resistance to oxidation erosion, good toughness and good resistance to oxidation and hot corrosion, NiCrAlY provides good resistance to oxidation and hot corrosion, while the chromium carbide provides excellent resistance to wear and erosion Used for delivery roll in the boiler, and for fuel rod mandrels, turbine components, forging tools, hot crushing rolls and forming dies Excellent wear and erosion protection up to 900°C (1,650°F)	--
LF313	Cr39Ni7C Atomized, Blended	106/45μm	AP	Resistance to high temperature, wearing, erosion and corrosion Ideal replacement for hard chrome, with high deposition efficiency Coatings provide excellent erosion and oxidation properties Usable on ball valves, hydraulic rods, boiler tubes, exhaust pipes, turbines, textile rolls and exhaust stacks Service temp. up to 900°C (1,650°F)	--
LF313-C	Cr39Ni7C Atomized, Blended	178/90μm	PTA	Resistance to high temperature, wearing, erosion and corrosion Ideal replacement for hard chrome, with high deposition efficiency Coatings provide excellent erosion and oxidation properties Usable on ball valves, hydraulic rods, boiler tubes, exhaust pipes, turbine, textile rolls and exhaust stacks Service temp. up to 900°C (1,650°F)	--
LF313-F	Cr39Ni7C Atomized, Blended	53/15μm	HV	Resistance to high temperature, wearing, erosion and corrosion Ideal replacement for hard chrome, with high deposition efficiency Coatings provide excellent erosion and oxidation properties Used on ball valves, hydraulic rods, boiler tubes, exhaust pipes, turbines, textile rolls and exhaust stacks Service temp. up to 900°C (1,650°F)	--
LF313-SC	Cr39Ni7C Atomized, Blended	90/10μm	HV	Resistance to high temperature, wearing, erosion and corrosion Ideal replacement for hard chrome, with high deposition efficiency Coatings provide excellent erosion and oxidation properties Usable on ball valves, hydraulic rods, boiler tubes, exhaust pipes, turbines, textile rolls and exhaust stacks Service temp. up to 900°C (1,650°F)	--
LF313-SF	Cr39Ni7C Atomized, Blended	30/10μm	HVAF	Resistance to high temperature, wearing, erosion and corrosion Ideal replacement for hard chrome, with high deposition efficiency Coatings provide excellent erosion and oxidation properties Usable on ball valves, hydraulic rods, boiler tubes, exhaust pipes, turbines, textile rolls and exhaust stacks Service temp. up to 900°C (1,650°F)	--
LF314	Cr3C2 15(FeCrAlY) Blended	106/10μm	AP	With high bonding strength, usable for rotors and stators of steam turbines Max. operating temperature 600°C (1,112°F)	--

TiC Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF361	TiC12Ni Clad	45/15μm	HV	Replacement of WC-12Co with same hardness and good resistance to wear at cheaper price, and not suitable for use in wet environment Max. Temp. 300°C (570°F)	--
LF362	TiC28Co8Cr Agglomerated & Sintered	45/15μm	HV	Forming harder coatings with better resistance to abrasion and less expensive in comparison with WC-10Co-4Cr Usable in wet and corrosive environment Service temp. up to 450°C (842°F)	--
LF461	Ni75B4C Clad	45/15μm	HV	Higher hardness and abrasive wear resistance than Al₂O₃, TiC and Cr₂O₃ Recommended to spray plunger piston of slurry pump Max. working Temp. 500°C (932°F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF361

TiC12Ni

Clad

45/15μm

HV

Replacement of WC-12Co with same hardness and good resistance to wear at cheaper price, and not suitable for use in wet environment
Max. Temp. 300°C (570°F)

--

LF362

TiC28Co8Cr

Agglomerated & Sintered

45/15μm

HV

Forming harder coatings with better resistance to abrasion and less expensive in comparison with WC-10Co-4Cr
Usable in wet and corrosive environment
Service temp. up to 450°C (842°F)

--

LF461

Ni75B4C

Clad

45/15μm

HV

Higher hardness and abrasive wear resistance than Al₂O₃, TiC and Cr₂O₃
Recommended to spray plunger piston of slurry pump
Max. working Temp. 500°C (932°F)

--

Al2O3 Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF401	Al2O3 98.0+ Fused & Crushed	45/15μm	AP	High purity alumina Recommended to use in semicon, electrical, photovoltaic industries and with high dielectric properties Chemically inert, resistant to acid, alkali and heat, and resistant to high temperature erosion and sliding wear LF401 SF of finer particle for spraying smoother coating with lower porosity Max. working temp. 1,650°C (3,000°F)	--
LF401AS	Al2O3 99.95 Agglomerated & Sintered	53/15μm	AP	High purity alumina Recommended to use in semicon, electrical, photovoltaic industries and with high dielectric properties Chemically inert, resistant to acid, alkali and heat, and resistant to high temperature erosion and sliding wear LF401 SF of finer particle for spraying smoother coating with lower porosity Max. working temp. 1,650°C (3,000°F)	--
LF401SF	Al2O3 99.5+ Fused & Crushed	31/3.9μm	AP	High purity alumina Recommended to use in semicon, electrical, photovoltaic industries and with high dielectric properties Chemically inert, resistant to acid, alkali and heat, and resistant to high temperature erosion and sliding wear LF401 SF of finer particle for spraying smoother coating with lower porosity Max. working temp. 1,650°C (3,000°F)	--
LF403	Al2O3 3TiO2 Fused & Crushed	45/15μm	AP	Resistant to particle wear and fretting wear, and to high temperature oxidation Coating formed is tougher than pure alumina Used in textile and artificial fiber industries, like thread and synthetic fiber production tooling, and also used for butterfly valves, electrical insulation and dielectric applications Service temp. up to 1,100°C (2,010°F)	--
LF403C	Al2O3 3TiO2 Clad	53/15μm	AP	Resistant to particle wear and fretting wear, and to high temperature oxidation Coating formed is tougher than pure alumina Used in textile and artificial fiber industries, like thread and synthetic fiber production tooling, and also used for butterfly valves, electrical insulation and dielectric applications Service temp. up to 1,100°C (2,010°F)	--
LF403F	Al2O3 3TiO2 Fused Crushed & Blended	35/5μm	AP	Resistant to particle and fretting wear, and to high temperature oxidation Coating formed is tougher than pure alumina Used in textile and artificial fiber industries, like thread and synthetic fiber production tooling, and also used for butterfly valves, electrical insulation and dielectric applications Service temp. up to 1,100°C (2,010°F)	--
LF406-1	Al2O3 13TiO2 Fused & Crushed	45/15μm	AP	Resistant to abrasion, sliding wear, oxidation, acids and alkalis Titania adds toughness but reduces hardness Used in textile and artificial fiber industries, like thread and synthetic fiber production tooling, and can work in acid-base medium, and also used for rollers in papermaking, for hydraulic parts, shaft sleeves and mechanical seals Service temp. up to 540°C (1,000°F)	--
LF406-2	Al2O3 13TiO2 Clad	45/15μm	AP	Resistant to abrasion, sliding wear, oxidation, acids and alkalis Titania adds toughness but reduces hardness Used in textile industry and artificial fiber industries, like thread and synthetic fiber production tooling, and can work in acid-base medium, and also used for rollers in papermaking, for hydraulic parts, shaft sleeves and mechanical seals Service temp. up to 540°C (1,000°F)	--
LF406-3	Al2O3 13TiO2 Fused & Crushed	53/15μm	AP	Resistant to abrasion, sliding wear, oxidation, acids and alkalis Titania adds toughness but reduces hardness Used in textile and artificial fiber industries, like thread and synthetic fiber production tooling, and can work in acid-base medium, and also used for rollers in papermaking, for hydraulic parts, shaft sleeves and mechanical seals Service temp. up to 540°C (1,000°F)	--
LF407	Al2O3 40TiO2 Fused, Crushed & Blended	75/30μm	AP	Coating formed is resistant to abrasion, fretting, particle erosion and dilute acids Good friction characteristics for hard bearing surfaces Ground/polished surfaces have low wettability Its wear resistance and corrosion stability are lower than that of LF406 but with good polishing property and resistant to fiber wear; Used in household pan, and for pump parts, shaft sleeves, mechanical seals, thread and synthetic fiber production tooling Service temp. up to 540°C (1,000°F)	--
LF408	Al2O3 30(Ni 20Al) Blended	90/10μm	AP	Coating formed is better than alumina in resisting abrasion, shock and thermal cycling Preventing the mismatch of thermal expansion for the intermediate layer in graded coatings May be used as an abrasive (cutting) coating in clearance control applications Service temp. up to 540°C (1,000°F)	--

Cr2O3 Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF415	Cr2O3 99.0 Sintered & Crushed	90/11μm	AP	Hard, wear resistant and chemically inert, Recommended to be used for exhaust manifold of engine Service temp. up to 540°C (1,000°F)	--
LF416	Cr2O3 99.5 Sintered & Crushed	45/15μm	AP	Hard, wear resistant and chemically inert Recommended to be used for anilox rolls Service temp. up to 540°C (1,000°F)	--
LF416-1	Cr2O3 99.6+ Sintered & Crushed	38/15	AP	Hard, wear resistant and chemically inert Recommended to be used for anilox rolls Service temp. up to 540°C (1,000°F)	--
LF416-2	Cr2O3 99.6+ Sintered & Crushed	90/15	AP	Hard, wear resistant and chemically inert Recommended to be used for anilox rolls Service temp. up to 540°C (1,000°F)	--
LF416-3	Cr2O3 99.6+ Sintered & Crushed	45/15μm	AP	Hard, wear resistant and chemically inert Recommended to be used for anilox rolls Service temp. up to 540°C (1,000°F)	--
LF417	Cr2O3 2TiO2 Fused and Crushed (Blocky)	125/11μm	AP	The coating formed is dense and resistant to particle wear, hard-face wear, erosion of grains and gas etching abrasion It’s insoluble in acid, alkali and alcohol solutions and used for rollers of pump seals, wearing rings and printing pattern rollers Service temp. up to 540°C (1,000°F)	--
LF418	Cr2O3 5SiO2 3TiO2 Fused and Crushed(Blocky)	90/11μm	AP	Coating formed is hard and dense with good tenacity and low frictional characteristics and higher resistance to mechanical shock, abrasion and erosion Unusually high ceramic toughness For pump components, wear rings, down-hole plungers, textile machinery parts and seals Service temp. up to 540°C (1,000°F)	--
LF418-2	Cr2O3 4SiO2 3TiO2 Agglomerated&Sintered	63/12μm	AP	Hard, dense, very wear resistant Unusually high ceramic toughness Resists, acids, alkalis, alcohols For pump components, wear rings, down-hole plungers, textile machinery parts, seals Service temp. up to 540°C (1,000°F)	--
LF419	Cr2O3 40TiO2 Blended	90/15μm	AP	With excellent resistance to abrasion, heat and corrosion, high fracture toughness, relatively lower hardness and good tenacity For wearing workpieces of high tenacity, like sucker rod couplings, doctor blades, machine tool chip breakers Service temp. up to 540°C (1,000°F)	--

TiO2 Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF425	99TiO2 Fused and Crushed (Blocky)	90/11μm	AP	Coating formed has a medium wear resistance and relatively low hardness It has stability to solutions other than acid-base solutions and doesn’t accumulate static electricity with no surface static charge Recommended to produce sputter targets, decorative coatings, mandrels, oxygen sensors and biomedical implants Service temp. up to 540°C (1,000°F)	--
LF426	TiO2 45Cr2O3 Blended	125/11μm	AP	With good resistance to wear, heat and erosion, it is hard with high fracture toughness, and with low frictional coefficient For sucker rod couplings, dry cell batter mandrels, cylinder bores, doctor blades and machine tool chip breakers Service temp. up to 540°C (1,000°F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF425

99TiO2

Fused and Crushed (Blocky)

90/11μm

AP

Coating formed has a medium wear resistance and relatively low hardness
It has stability to solutions other than acid-base solutions and doesn’t accumulate static electricity with no surface static charge
Recommended to produce sputter targets, decorative coatings, mandrels, oxygen sensors and biomedical implants
Service temp. up to 540°C (1,000°F)

--

LF426

TiO2 45Cr2O3

Blended

125/11μm

AP

With good resistance to wear, heat and erosion, it is hard with high fracture toughness, and with low frictional coefficient
For sucker rod couplings, dry cell batter mandrels, cylinder bores, doctor blades and machine tool chip breakers
Service temp. up to 540°C (1,000°F)

--

ZrO2 Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF435	ZrO25CaO Fused & Crushed	90/15μm	AP	Forming thermal barrier coating, and used for components in the hot section of turbines Corrosion and lubrication resistance in molten metal Used for diesel engine plunger, valve cylinder sleeve head, cast molding coating, Service temp. up to 900°C (1,650°F)	--
LF438	ZrO225CeO2 2.5Y2O3 Agglomerated & Plasma Densified	125/11μm	AP	With good thermal barrier performance, better corrosion stability performance and high temperature resistance in environment of sodium, sulfur and chlorine For components in the hot section of turbines Service temp. up to 1,250°C (2,280°F)	--
LF439	ZrO218TiO210Y2O3 Agglomerated	75/5μm	AP	With good abrasion resistance, red hardness, strong resistance to thermal shock and good corrosion resistance to sulfur, sodium and chlorine For hard bearing surfaces on liners, cylinder bores, piston rings and crowns, exhaust valves and turbine blades Service temp. up to 980°C (1,800°F)	--
LF440	ZrO28Y2O3 Agglomerated	106/45μm	AP	In spherical form, it has a good mobility, good chemical homogeneity and high purity; the nano initial powder and the tubular form enable it to have a good performance in thermal barrier and insulation Used in combustion chamber of a turbine and as thermal barrier coating of air engine units Service temp. up to 1,280°C (2,336°F)	--
LF441	ZrO28Y2O3 Agglomerated & Plasma Densified	125/11μm	AP	In spherical form, it has a good mobility, good chemical homogeneity and high purity, the nano initial powder and the tubular form enable it to have a good performance in thermal barrier and insulation Used in combustion chamber of a turbine and as thermal barrier coating of air engine units Service temp. up to 1,280°C (2,336°F)	--
LF442	ZrO220Y2O3 Agglomerated	106/15μm	AP	Apply to a higher temperature, with erosion resistance to a recommended temperature of over 845°C and apply as the thermal barrier coating on rocket nozzles and missile nose cones to resist particle erosion Service temp. up to 980°C (1,800°F)	--

Y2O3 Based

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF456	99.9 Y2O3 Agglomerated & Sintered	90/11μm	AP	High temperature resistant and antioxidant, superior dielectric and electrical insulation; highly resistant to plasma and fluoride etching, stable at high temperatures Used in electronic industry and the protection, like in semi-conductor production tooling, linings for graphite molds or in hard cemented carbide The higher the purity, the better the performance Service temp. up to 1,650°C (3,000°F)	--

Product

Chemistry
Manufacture

Particle
Size

Process

Application

Download

LF456

99.9 Y2O3

Agglomerated & Sintered

90/11μm

AP

High temperature resistant and antioxidant, superior dielectric and electrical insulation; highly resistant to plasma and fluoride etching, stable at high temperatures
Used in electronic industry and the protection, like in semi-conductor production tooling, linings for graphite molds or in hard cemented carbide
The higher the purity, the better the performance
Service temp. up to 1,650°C (3,000°F)

--

Abradables

Product	Chemistry Manufacture	Particle Size	Process	Application	Download
LF105	Al8Si20BN Clad	212/22μm	AP	High-quality abradable coating material Used for jet engine compressor Working temperature up to 480°C (896°F)	--
LF106	Al7Si22Graphite Clad	125/5μm	CP	High-quality abradable coating material Used for jet engine compressor Working temperature up to 480°C (896°F)	--
LF107	Al6Si24Graphite Clad	180/8μm	AP	High-quality abradable coating material Used for jet engine compressor Working temperature up to 315°C (599°F) to 425°C (797°F)	--
LF108	Al5Si45Graphite Clad	180/8μm	AP	High-quality abradable coating material Used for jet engine compressor Working temperature up to 315°C (599°F) to 425°C (797°F)	--
LF109	Al7Si40Polyester Clad	180/45	AP	Internal and external air sealing of high and low pressure air compressor Replace silver and RTV rubber as air sealing Compressor abradable workpiece whose operating temperature is 325℃-350℃（615℉-660℉）	--
LF132	Cu10Al Clad	106/45μm	AP	Used for piston guide rail, shifting fork, compressor air seal Working temperature 650°C (1200°F)	--
LF140	Cu9.5Al7.5(MoS2) Clad	125/45μm	AP	Self-adhesion and self-lubricating coating Used for repairing of bearing and copper-based alloy Service temp. up to 650°C (1200°F)	--
LF141	Cu30Graphite Clad	105/45μm	CP	Electrical contact material and low-friction material Working temperature up to 315°C (599°F)	--
LF225	Ni30Graphite Clad	90/30μm	AP CP	abradable materials for clearance control coatings in the compressor section of turbine engines Higher graphite content enhances lubricity; higher nickel content enhances erosion resistance Working temperature up to 480°C (896°F)	--
LF226	Ni15Graphite Clad	106/30μm	CP	Compressor inter-stage coating Higher graphite content enhances lubricity; higher nickel content enhances erosion resistance Working temperature up to 480°C (896°F)	--
LF227	Ni20Graphite Clad	106/45μm	CP	Compressor inter-stage coating Higher graphite content enhances lubricity; higher nickel content enhances erosion resistance Working temperature up to 480°C (896°F)	--
LF228	Ni25Graphite Clad	90/30μm	CP	Compressor inter-stage coating Higher graphite content enhances lubricity; higher nickel content enhances erosion resistance Working temperature up to 480°C (896°F)	--
LF229	Ni 4Cr 4Al 21Bentonite Chemically Clad	150/45	AP CP	Turbine high pressure compressor abradable Finer cuts produce harder, more erosion resistant coatings Similar products differ by OEM specification approvals Service temp. up to 650°C (1200°F)	--
LF231	Ni14Cr8Fe5BN3.5Al Clad	105/45μm	CP	Gas compressor abradable coating Working temperature up to 480°C (896°F)	--
LF235-2	Ni20-25(MoS2) Clad	125/45μm	AP	Usable as motive sealing element and low-friction material Usable as self-lubricating coating, like bearing Working temperature up to 315°C (599°F)	--
LF238	Ni 9Al 25BN Clad	180/53	CP AP	Abradable for high temperature and high pressure seals Excellent thermal shock resistance and high hardness Service up to 700°C（1,292°F）	--
LF245	Al 9Si 6BN 20Polyester Blended	125/11μm	AP	Turbine fan and front compressor abradable Optimal balance of abradability, erosion resistance and hardness	--
LF246	ZrO2 7.5Y2O3 4Polyester Agglomerated	176/11μm	AP	Turbine hot section abradable Durabrade 2192 usable to run against untipped blades under specific conditions Polymer controls coating porosity Polymer can be removed via post-coat heat treatment	--
LF247	Co 24Ni 16Cr 6Al 0.3Y 7BN 14Polyester Blended	176/7.8μm	AP	Abradable for high pressure turbine compressors, labyrinth shaft seals and disk seals Excellent oxidation and corrosion resistance Service up to 550°C（1025°F）to run against titanium; up to 750°C(1390°F) to run against Inconel and stainless steel Polymer can be removed via post-coat heat treatment	--
LF248	Co 25Ni 16Cr 6Al 0.3Y 4BN 15Polyester Blended	176/11μm	AP	Abradable for high pressure turbine compressors, labyrinth shaft seals and disk seals Excellent oxidation and corrosion resistance Service up to 550°C（1025°F）to run against titanium; up to 750°C(1390°F) to run against Inconel and stainless steel Polymer can be removed via post-coat heat treatment	--
LF345	Ni 25Bentonite Chemically Clad	150/53μm	CP	Compressor inter-stage coating Higher bentonite content enhances lubricity; higher nickel content enhances erosion resistance Working temperature up to 480°C (896°F)	--

Ag: Silver	hBN: Hexagonal Boron Nitride	P: Phosphorus
Al: Aluminum	Hf: Hafnium	Pb: Lead
B: Boron	In: Indium	Sb: Antimony
BN: Boron Nitride	LSCF: Lanthanum Strontium Cobalt Ferrite	Si: Silicon
C: Carbon or Carbide	LSM: Lanthanum Strontium Manganite	Sn: Tin
Ca: Calcium	M: Metal (generic)	Ta: Tantalum
cBN: Cubic Boron Nitride	MCO: Manganese Cobalt Oxide	Ti: Titanium
Co: Cobalt	Mg: Magnesium	V: Vanadium
Cr: Chromium	Mn: Manganese	W: Tungsten
Cu: Copper	Mo: Molybdenum	Y: Yttrium
Dy: Dysprosium	N: Nitrogen	Yb: Ytterbium
Fe: Iron	Nb (Cb): Niobium	Zn: Zinc
Gd: Gadolinium	Ni: Nickel	Zr: Zirconium
H: Hydrogen	O: Oxygen

UCT Thermal Spray Materials Guide